model nr.: A-9080W/B-6088
Brand: Xuchuan
Oprindelsessted: Kina
Typer Af: Syntetisk harpiks og plast
Application: Outsole, slippers, wedge shoes
Keywords: Lady shoe sole
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Package(kg): 18/20kg
Appearence: liquid
Codes: A-9080W/B-6088
Brand: Xuchuan
Application | shoe sole |
Keywords | Lady shoe sole |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Low Density Shoe System Characteristic |
: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
Application: Outsole, slippers, wedge shoes |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Raw Material Polyester Resin Materials preheat |
|||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
Typical processing parameters & Reaction parameter. |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
|
Xuchuan Chemical, der blev oprettet i 2007, er selskabsregistreret kapital RMB 500 millioner. De vigtigste produkter er alle intervaller polyester polyol, polyurethanharpiks til sko, vandbaseret og opløsningsmiddelfri polyurethanharpikser til kunstigt læder, polyurethanbinding af klæbemidler og polyurethan hot smelte klæbemidler.
Nu har Xuchuan 4 moderne produktionsbaser, produktionskapacitet nåede 630.000 ton om året, produkter, der eksporteres til 32 lande og regioner i verden.
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.
Udfyld mere information, så det kan komme i kontakt med dig hurtigere
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.