model nr.: XC-9080W/XC-6088W
Brand: Xuchuan Chemical
Oprindelsessted: Kina
Application: Outsole, slippers, wedge shoes
Code: XC-9080W/XC-6088W
Keywords: water soluble polyurethane resin
Appearance: Liquid
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Application | shoe sole |
Keywords | water soluble polyurethane resin |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
Application: Outsole, slippers, wedge shoes |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Materials preheat |
|||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
Typical processing parameters & Reaction parameter. |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
Physical propertiesShoe Sole Pu Chemical |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
Demold time may be prolonged with the increase of sole thickness. |
|||||||
|
|||||||
|
Disse fysiske data erhverves ved at teste en prøve på 6 mm tyk.
Data, der er anført ovenfor, er kun til reference. Detaljedataene udsættes for praktisk produktion. Hvis andre anmodninger om fysiske egenskaber, bedes du kontakte os.
PU -system til skosål, klæbemiddel til sko, CPU, TPU, polyesterpolyol, PU -harpiks til blæk, pur varm smelte klæbemiddel, klæbemiddel til fleksibel pakke, PU -harpiks til syntetisk læder
Xuchuan Chemical, der blev oprettet i 2007, er selskabsregistreret kapital RMB 500 millioner. De vigtigste produkter er alle intervaller polyester polyol, polyurethanharpiks til sko, vandbaseret og opløsningsmiddelfri polyurethanharpikser til kunstigt læder, polyurethanbinding af klæbemidler og polyurethan hot smelte klæbemidler.
Nu har Xuchuan 4 moderne produktionsbaser, produktionskapacitet nåede 630.000 ton om året, produkter, der eksporteres til 32 lande og regioner i verden.
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.
Udfyld mere information, så det kan komme i kontakt med dig hurtigere
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.