Flydende polyurethan harpiks damer sandaler til midt-sålesko
Get Latest PriceBetalings type: | L/C,T/T |
Incoterm: | FOB,CIF |
Min. Bestille: | 1000 Kilogram |
Transport: | Ocean |
Havn: | Shanghai ,Taicang,Ningbo |
Betalings type: | L/C,T/T |
Incoterm: | FOB,CIF |
Min. Bestille: | 1000 Kilogram |
Transport: | Ocean |
Havn: | Shanghai ,Taicang,Ningbo |
model nr.: A-2001/B-8580
Brand: Xuchuan
Oprindelsessted: Kina
Typer Af: Syntetisk harpiks og plast
Brand Name: Xuchuan
Appearence: Liquid
Model Number: A-2001/B-8580
Application: Insole and low density mid-sole
Characteristic: Good handle, low density and good dimension stability, high elasticity
Purity: 100
Keywords: Polyurethane for footwear sole
Salgsenheder | : | Kilogram |
Pakketype | : | Polyol: 210 & 18 kg/tromle isocyanat: 225 & 20 kg/tromleadditiver: 20 kg/tromle |
Eksempel på billede | : |
PRODUKT BESKRIVELSE
Polyolisocyanat til mid-sole/polyester polyol isocyanat/polyurethan råmaterialer
Hovedsageligt for branchen er skomagerende , og er altid forpligtet til at levere produktstøttelsesløsninger til kundernes mellem- og lavere rækkevidde.
Flydende polyurethan harpiks damer sandaler øvre materiale indersål til mid-solesko
Application | shoes insole |
A/B Materials Temperatures (℃) | 40~45/38~42 |
A+C/B Mix ratio (By weight) | 100/74~76 |
Cream Time (s) | 7~9 |
End of Rise Time (s) | 50~60 |
Free Rise Foam Density(g/cm3) | 0.13~0.16 |
Mold Temperature (℃) | 45~55 |
Molded Density (g/cm3) | 0.30~0.40 |
Hardness (Shore C ) | 35~45 |
Tensile strength(MPa) | Tensile strength(MPa) |
Characteristic: Good handle, low density and good dimension stability, high elasticity |
|||||||
Application: Insole and low density mid-sole |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
||
A-2001 |
Liquid |
1000~1400 |
1.01~1.02 |
18 |
|||
B-8580 |
Yellowish transparent liquid or waxy |
600~1000 |
1.08~1.2 |
20 |
|||
Materials preheat |
|||||||
A-2001: preheated at 50~60℃ for 8~10 hours. |
|||||||
B-8580: preheated at 50~60℃ for 8~12 hours. |
|||||||
Typical processing parameters & Reaction parameter |
|||||||
Items |
A/B Materials Temperatures |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/74~76 |
7~9 |
50~60 |
0.13~0.16 |
45~55 |
4~5 |
The adding content of C-2 should be 300g±20g/18kg. |
|||||||
The adding content of water should be 0~90g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength(MPa) |
Elongation (%) |
Tear Strength |
/ |
|
Physical properties |
0.30~0.40 |
35~45 |
4.0~6.0 |
300~380 |
18~26 |
||
Demold time may be prolonged with the increase of sole thickness |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Xuchuan Chemical, der blev oprettet i 2007, er selskabsregistreret kapital RMB 500 millioner. De vigtigste produkter er alle intervaller polyester polyol, polyurethanharpiks til sko, vandbaseret og opløsningsmiddelfri polyurethanharpikser til kunstigt læder, polyurethanbinding af klæbemidler og polyurethan hot smelte klæbemidler.
Nu har Xuchuan 4 moderne produktionsbaser, produktionskapacitet nåede 630.000 ton om året, produkter, der eksporteres til 32 lande og regioner i verden.
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.
Udfyld mere information, så det kan komme i kontakt med dig hurtigere
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.