model nr.: A-2260/B-8580
Brand: Xuchuan Chemical
Oprindelsessted: Kina
Typer Af: Syntetisk harpiks og plast
Application: Outsole and mid-sole
Characteristic: Good handle, low density and good dimension stability
Appearance: Liquid
PRODUKT BESKRIVELSE
Polyurethan råvarer
Sko sål PU -kemikalie
Application | shoe sole |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 40~50 |
Free Rise Foam Density(g/cm3) | 0.15~0.25 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | 2.5~3.5 |
Molded Density (g/cm3) | 0.30~0.45 |
Hardness(Shore A ) | 43~58 |
Tensile strength(MPa) | 1.5~4.5 |
Elongation(%) | 250~400 |
Polyurethan til fodtøjsål:
Densitet: 300 ~ 500 kg/m3.
Hårdhed: 45 ~ 75shore A.
God kompatibilitet med pigmenter.
Bredt forhold.
Characteristic: Good handle, low density and good dimension stability |
|||||||
Application: Outsole and mid-sole |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-2260 |
Cream white liquid |
800~1200 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-8580 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Materials preheat |
|||||||
A-2260: preheated at 50~60℃ for 8~10 hours |
|||||||
B-8580: preheated at 50~60℃ for 8~12 hours |
|||||||
Typical processing parameters & Reaction parameter |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/96~98 |
6~8 |
40~50 |
0.15~0.25 |
45~55 |
2.5~3.5 |
The adding content of C-2 should be 270g±20g/18kg |
|||||||
The adding content of water should be 0~100g/18kg according to the reality |
|||||||
The adding content of hardener should be changed according to the reality |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness (Shore A ) |
Tensile strength (MPa) |
Elongation (%) |
Tear Strength (kN/m) |
Ross Flexing (room temperature) ( 40,000 times) |
/ |
/ |
|||||||
/ |
|||||||
Physical properties |
0.30~0.45 |
43~58 |
1.5~4.5 |
250~400 |
10~26 |
No crack |
/ |
Demold time may be prolonged with the increase of sole thickness |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Xuchuan Chemical, der blev oprettet i 2007, er selskabsregistreret kapital RMB 500 millioner. De vigtigste produkter er alle intervaller polyester polyol, polyurethanharpiks til sko, vandbaseret og opløsningsmiddelfri polyurethanharpikser til kunstigt læder, polyurethanbinding af klæbemidler og polyurethan hot smelte klæbemidler.
Nu har Xuchuan 4 moderne produktionsbaser, produktionskapacitet nåede 630.000 ton om året, produkter, der eksporteres til 32 lande og regioner i verden.
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.
Udfyld mere information, så det kan komme i kontakt med dig hurtigere
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.