XUCHUAN CHEMICAL(SUZHOU) CO., LTD
| Betalings type: | L/C,T/T |
| Incoterm: | FOB,CIF |
| Min. Bestille: | 3 Ton |
| Transport: | Ocean,Land,Air |
| Havn: | Shanghai |
model nr.: A-1166,B-6003
Brand: Xuchuan Chemical
Oprindelsessted: Kina
Typer Af: Syntetisk harpiks og plast
Brand Name: Xuchuan
Appearence: liquid
Model Number: A-1166,B-6003
Application: Tire(doule density), marine fender and shock absorption mat
Characteristic1: Good hydrolysis resistance and high resilience
Characteristic2: temperature has little effect on hardness
| Salgsenheder | : | Ton |
| Pakketype | : | 220 kg/tromme |
| Eksempel på billede | : |
|
PU -hjulkemikalier
Karakteristisk: god hydrolysemodstand og høj modstandsdygtighed, temperaturen har ringe indflydelse på hårdheden
Anvendelse : Dæk (Doule Density), Marine Fender og Shock Absorption Mat
Hjulpolyurethan støbning harpiks typiske egenskaber ved PU -matrix
| Name of products | Appearance |
Viscoscity (mPa·s/40℃) |
Density (g·cm-³/40℃) |
Package (kg) |
| A-1166 | (>25℃) Liqud | 700-1100 | 1.01-1.02 | 200 |
| B-6003 | Yellowish Transparent liquid | 500-900 | 1.08-1.2 | 200 |
Brugerdefinerede hjul PU -materialer forvarmning
A-1166 : Forvarmet ved 50 ℃ ~ 60 ℃ i 8-12 timer
B-6003 : Forvarmet ved 60 ℃ ~ 70 ℃ i 8-12 timer
Typiske behandlingsparametre og reaktionsparameter
| Items |
A/B Materials Temperatures (℃) |
Out-layer Mix ratio A+C/B (By weight) |
In-layer Mix ratio A+C/B (By weight) |
Cream Time (s) |
End of Rise Time (s) |
Out-layer Free Rise Foam Density (g/cm³) |
In-layer Free Rise Foam Density (g/cm³) |
Mold Temperature (℃) |
Demold Time (min) |
| Parameter | 45-50/40-45 | 100/70 | 100/77 | 4-6 | 30-40 | 0.9-1.1 | 0.5-0.55 | 45-55 | 3-4 |
Det tilføjende indhold af katalysator (A: 200 kg): ud-lag --- C-2 4 ~ 4,5 kg C-8 0,5 ~ 1 kg
I-lag ----- C-2 3 ~ 3,5 kg C-8 0,5 ~ 1,1 kg
Det tilføjende indhold af hærder skal være 400 ~ 500 g/200 kg i henhold til virkeligheden
Det tilføjende indhold af hærder CF skal være 0 ~ 3 kg/200 kg i henhold til virkeligheden
Fysiske egenskaber
| Items |
Molded Density (g/cm³)
|
Hardness (Shore A) |
Tear Strength (kN/m)
|
Tensile Strength (MPa) |
||||
|
Physical properties
|
Out-layer | In-layer | Out-layer | In-layer | Out-layer | In-layer | Out-layer | In-layer |
| 0.9-1.1 | 0.5-0.6 | 70-75 | 55-60 | 21-25 | 15-18 | 5.6-7.5 | 4.0-5.4 | |
|
Criterion |
ASTM D792 | ASTM D2240 | ASTM D624 | ASTM D412 | ||||
| Items | DIN abrasion(mm³) | Hydrolyzed properties 70℃*95% relative humidity Physical properties retention rate |
Ross Flexing -90°(-20℃) |
||
| Out-layer | In-layer | 168 hours | 336 hours | 100000 times no crack | |
| Physical properties | 70-100 | 100-200 | no significant decline | above 85% | |
Disse fysiske data erhverves ved at teste en prøve på 6 mm tyk og 0,5 g/cm³ densitet
Prøvens hårdhed ved forskellig temperatur
| Items |
Molded Density (g/cm³) |
20℃ | 10℃ | 0℃ | -4℃ | -10℃ | -20℃ |
|
Hardness (Shore A) |
0.5 | 50 | 50 | 51 | 51 | 52 | 54 |
Data, der er anført ovenfor, er kun til reference. Dataene udsættes for praktisk produktion. Hvis andre anmodninger om fysiske egenskaber, bedes du kontakte os.
Xuchuan Chemical, der blev oprettet i 2007, er selskabsregistreret kapital RMB 500 millioner. De vigtigste produkter er alle intervaller polyester polyol, polyurethanharpiks til sko, vandbaseret og opløsningsmiddelfri polyurethanharpikser til kunstigt læder, polyurethanbinding af klæbemidler og polyurethan hot smelte klæbemidler.
Nu har Xuchuan 4 moderne produktionsbaser, produktionskapacitet nåede 630.000 ton om året, produkter, der eksporteres til 32 lande og regioner i verden.
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.
Udfyld mere information, så det kan komme i kontakt med dig hurtigere
Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.
Contact Now