Hjem> Produkter> Polyurethan -system til skosål> Polyurethan -system til sandaler og hjemmesko> Polyurethanharpiks Polyolisocyanat til skoinsål
Polyurethanharpiks Polyolisocyanat til skoinsål
Polyurethanharpiks Polyolisocyanat til skoinsål
Polyurethanharpiks Polyolisocyanat til skoinsål
Polyurethanharpiks Polyolisocyanat til skoinsål
Polyurethanharpiks Polyolisocyanat til skoinsål
Polyurethanharpiks Polyolisocyanat til skoinsål

Polyurethanharpiks Polyolisocyanat til skoinsål

Get Latest Price
Betalings type:L/C,T/T,D/P
Incoterm:FOB,CFR,CIF
Min. Bestille:1000 Kilogram
Transport:Ocean
Havn:Shanghai
Produktattributter

model nr.A-2001/B-8580

BrandXuchuan Chemical

OprindelsesstedKina

Typer AfSyntetisk harpiks og plast

ApplicationShoe Insole, Insole and low density mid-sole

CharacteristicGood handle, low density and good dimension stability, high elasticity

AppearanceLiquid

CodeA-2001/B-8580

BrandXuchuan

Emballage og levering
Salgsenheder : Kilogram
Pakketype : 20 & 225 kg/tromme
Eksempel på billede :
Produkt beskrivelse

PRODUKT BESKRIVELSE

Sko sål PU -kemikalie

Vandaktiveret polyurethanharpiks Materialeplade Sandaler Sål til skoinsål

Polyurethan råvarer

Råmateriale polyesterharpiks

Produktdetaljer

Application shoes insole
A/B Materials Temperatures (℃) 40~45/38~42
A+C/B Mix ratio (By weight) 100/74~76
Cream Time (s) 7~9
End of Rise Time (s) 50~60
Free Rise Foam Density(g/cm3) 0.13~0.16
Mold Temperature (℃) 45~55
Molded Density (g/cm3) 0.30~0.40
Hardness (Shore C ) 35~45
Tensile strength(MPa) Tensile strength(MPa)

Characteristic: Good handle, low density and good dimension stability, high elasticity

Application: Insole and low density mid-sole

Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40)

Density 

(g·cm-3/40)

Package(kg)

/

A-2001

Liquid

1000~1400

1.01~1.02

18

B-8580

Yellowish transparent liquid or waxy

600~1000

1.08~1.2

20

Materials preheat

A-2001:  preheated at 50~60 for 8~10 hours.  

B-8580:  preheated at 50~60 for 8~12 hours.

Typical processing parameters & Reaction parameter

Items

A/B Materials Temperatures
(℃)

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature
(℃)

Demold Time(min)

Parameter

40~45/38~42

100/74~76

7~9

50~60

0.13~0.16

45~55

4~5

The adding content of C-2 should be 300g±20g/18kg.

The adding content of water should be 0~90g/18kg according to the reality.

Physical properties

Items

Molded Density (g/cm3)

Hardness
(Shore C )

Tensile strength(MPa)

Elongation (%)

Tear Strength
(kN/m)

/

Physical  properties

0.30~0.40

35~45

4.0~6.0

300~380

18~26

Demold time may be prolonged with the increase of sole thickness

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.


Firmaoversigt

company company

Xuchuan Chemical, der blev oprettet i 2007, er selskabsregistreret kapital RMB 500 millioner. De vigtigste produkter er alle intervaller polyester polyol, polyurethanharpiks til sko, vandbaseret og opløsningsmiddelfri polyurethanharpikser til kunstigt læder, polyurethanbinding af klæbemidler og polyurethan hot smelte klæbemidler.

Nu har Xuchuan 4 moderne produktionsbaser, produktionskapacitet nåede 630.000 ton om året, produkter, der eksporteres til 32 lande og regioner i verden.

Værksted
Certifikat
Udstilling
F & U -afdeling
Kooperative kunder
Pakning og forsendelse


FAQ
Send forespørgsel
*
*

Vi kontakter dig øjeblikkeligt

Udfyld mere information, så det kan komme i kontakt med dig hurtigere

Beskyttelseserklæring: Dit privatliv er meget vigtigt for os. Vores virksomhed lover ikke at videregive dine personlige oplysninger til ethvert udstrækning uden dine eksplicitte tilladelser.

Sende