Hjem> Produkter> Polyurethan -system til skosål> Polyurethan -system til sikkerhedssko sål> Polyurethanharpiks til sikkerhedssko
Polyurethanharpiks til sikkerhedssko
Polyurethanharpiks til sikkerhedssko
Polyurethanharpiks til sikkerhedssko
Polyurethanharpiks til sikkerhedssko
Polyurethanharpiks til sikkerhedssko

Polyurethanharpiks til sikkerhedssko

$2≥1Kilogram

Betalings type:L/C,T/T,D/P
Incoterm:FOB,CFR,CIF
Min. Bestille:1 Kilogram
Transport:Ocean
Havn:Shanghai
Produktattributter

BrandXuchuan

ApplicationFootwear

Emballage og levering
Salgsenheder : Kilogram
Pakketype : 20 & 225 kg/rom
Sko Produktion.mp4
Produkt beskrivelse
Polyurethanharpiks til sikkerhedssko

Polyurethan til sikkerhedssko -sål, god slidbestandighed, høj styrke og sammenhængende kraft

Produktdetaljer

Application Safety shoe sole
polyol isocyanate Polyurethane raw materials
A/B Materials Temperatures (℃) 40~45/40~45
Mold Temperature (℃) 45~55
Demold Time (min)) 3~5
(room temperature) Flexing resistance 100,000 times no crack

Typical processing parameters & Reaction parameter

Items

A/B Materials Temperatures
(℃)

A+C/B Mix ratio
(By weight)

Cream Time
 (s)

End of Rise Time (s)

Parameter

40~45/40~45

sole

mid-sole

sole

mid-sole

40~50

100/69~71

100/77~79

6~8

6~7

 

Items

Free Rise Foam Density
(g/cm3)

Mold Temperature
(℃)

Demold Time
(min))

/

Parameter

Sole

mid-sole

45~55

3~5

0.47~0.50

0.23~0.26

The adding content of C-2 should be 300g±20g/18kg

The adding content of water and hardener should be changed according to the reality

sole:    H2O 20~30g/18kg     Hardener 0~400g/18kg               

mid-sole: H2O 50~55g/18kg     Hardener 0~600g/18kg    

Physical properties

Items

Molded Density (g/cm3)

Hardness
(Shore A )

Tensile strength(MPa)

Elongation (%)

Physical  properties

sole

mid-sole

sole

mid-sole

sole

mid-sole

sole

mid-sole

0.9~1.1

0.45~0.55

62~72

45~55

8.0~11.0

3.9~7.9

550~750

520~690

Items

Tear Strength
(kN/m)

 (room temperature)

Williams abrasion
(cc/php)

Adhesion between sole and mid-sole
(kg/cm)

Flexing resistance

 (Break length,0mm)

Physical  properties

sole

mid-sole

100,000 times no crack

sole

mid-sole

40~60

25~40

16~27

60~100

-

Demold time may be prolonged with the increase of sole thickness

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.


FIRMAPROFIL

PRODUKTIONS PROCES
CERTIFICERING
Emballage og forsendelse
FAQ

PU -system til skosål, klæbemiddel til sko, CPU, TPU, polyesterpolyol, PU -harpiks til blæk, pur varm smelte klæbemiddel, klæbemiddel til fleksibel pakke, PU -harpiks til syntetisk læder


Send forespørgsel
*
*